Spheroidal graphite cast iron roll

      Properties

Thanks to its higher content of Ni and Mo alloys, pearlite, basinite and martensite matrixes with excellent performance are produced. The graphite si spherical form, demonstraing good heat transfer property and high tensile strength. Through changing the struture into basinite of marensite matrix, chemical compostion of needly-like spherical iron of heat treatment, a dense reticular primary cementite with high wear-resistance is produced

 Centrifugal                                                           static

  pearlitic                                                      bainitic

    Chemical Analysis

Designation of rolls
C
Si
Mn
P
S
Ni
Cr
Mo
Mg
CrMo semi-chilled SG cast iron rolls
2.9/3.6
0.8/2.5
0.4/1.2
≤0.25
≤0.03
 
0.2/0.6
0.2/0.6
>0.04
CrMo indefinite chilled SG cast iron rolls
2.9/3.6
0.8/2.5
0.4/1.2
≤0.25
≤0.03
 
0.2/0.6
0.2/0.6
>0.04
NiCrMo indefinite chilled SG cast iron rolls (I)
2.9/3.6
0.8/2.5
0.4/1.2
≤0.25
≤0.03
0.5/1.0
0.2/0.6
0.2/0.6
>0.04
NiCrMo indefinite chilled SG cast iron rolls (II)
2.9/3.6
0.8/2.5
0.4/1.2
≤0.25
≤0.03
1.0/2.0
0.3/1.2
0.2/0.8
>0.04
Pearlitic nodular cast iron rolls (I)
2.9/3.6
1.4/2.2
0.4/1.0
≤0.15
≤0.03
1.5/2.0
0.1/0.6
0.2/0.8
>0.04
Pearlitic nodular cast iron rolls (II)
2.9/3.6
1.2/2.0
0.4/1.0
≤0.15
≤0.03
2.0/2.5
0.2/1.0
0.2/0.8
>0.04

Pearlitic nodular cast iron rolls (III)

 2.9/3.6

 1.0/2.0

 0.4/1.0

 ≤0.15

 ≤0.03

 2.5/3.0

 0.2/1.2

0.2/0.8

 >0.04

 bainitic nodular cast iron rolls (I)

 2.9/3.6

 1.2/2.2

 0.2/0.8

 ≤0.10

 ≤0.03

 3.0/3.5

0.2/1.0

 0.5/1.0

 >0.04

 bainitic nodular cast iron rolls (II)

 2.9/3.6

 1.2/2.0

 0.2/0.8

 ≤0.10

 ≤0.03

 3.5/4.5

 0.3/1.5

 0.5/1.0

 >0.04

         
        Physical Properties
Designation of rolls
Barrel hardness (HSD)
Neck hardness (HSD)
Tensile strength (MPa)
CrMo semi-chilled SG cast iron rolls
40~55
32~50
>300
CrMo indefinite chilled SG cast iron rolls
55~70
35~55
>300
NiCrMo indefinite chilled SG cast iron rolls (I)
48~70
35~55
>320
NiCrMo indefinite chilled SG cast iron rolls (II)
48~70
35~55
>320
Pearlitic nodular cast iron rolls (I)
45~55
35~55
>450
Pearlitic nodular cast iron rolls (II)
55~65
35~55
>450

 Pearlitic nodular cast iron rolls (III)

 62~72

 35~55

 >450

  bainitic nodular cast iron rolls (I)

 55~78

 32~45

 >350

 bainitic nodular cast iron rolls (II)

 60~80

32~45 

 >350

 
        Microstructure

Designation of rolls
Microstructure
CrMo semi-chilled SG cast iron rolls
Pearlite + cementite + SG + small percentage fermite
CrMo indefinite chilled SG cast iron rolls
Pearlite + cementite + SG
NiCrMo indefinite chilled SG cast iron rolls (I)
Pearlite + cementite + SG
NiCrMo indefinite chilled SG cast iron rolls (II)
Fine pearlite + cementite + SG
Pearlitic nodular cast iron rolls (I)
pearlite + cementite + small percentage fermite
Pearlitic nodular cast iron rolls (II)
pearlite + cementite + small percentage fermite

 Pearlitic nodular cast iron rolls (III)

 pearlite + cementite + small percentage fermite

  bainitic nodular cast iron rolls (I)

bainite + cementite + SG

 bainitic nodular cast iron rolls (II)

bainite + cementite + SG

 
        Application

Designation of rolls
Application
CrMo semi-chilled SG cast iron rolls
Section mill, bar mill, roughing stands of wire-rod mill, work roll of rail mill
CrMo indefinite chilled SG cast iron rolls
Section mill, bar mill, intermediate and finishing stands of wire-rod mill
NiCrMo indefinite chilled SG cast iron rolls (I)
Section mill, bar mill, intermediate and finishing stands of wire-rod mill
NiCrMo indefinite chilled SG cast iron rolls (II)
Section mill, bar mill, intermediate and finishing stands of wire-rod mill
Pearlitic nodular cast iron rolls (I)
roughing stands of bar mill and wire-rod mill
Pearlitic nodular cast iron rolls (II)
roughing stands of bar mill and wire-rod mill

 Pearlitic nodular cast iron rolls (III)

 roughing stands of bar mill and wire-rod mill

  bainitic nodular cast iron rolls (I)

 roughing stands of bar mill and wire-rod mill

 bainitic nodular cast iron rolls (II)

 roughing stands of bar mill and wire-rod mill

 

Suite 1909-1910 Tower A, Raycom Wangjing Center, Chaoyang Beijing 100102

Contact Us: liweifeng@camet.com.cn kangxiangguang@camet.com.cn  
Tel: +86-10-8858-8886     Fax: +86-10-8858 9776
 Beijing public network security 11010802010608
Jing ICP Bei no.12052076